1. TEMPERATURE CLASSIFICATION
COM alumina silicate swinging fiber cotton 1100 ℃
ST alumina silicate swinging fiber cotton 1260 ℃
HP alumina silicate swinging fiber cotton 1260 ℃
HA alumina silicate swinging fiber cotton 1360 ℃
HAZ alumina silicate swinging fiber cotton 1360 ℃
HZ alumina silicate swinging fiber cotton 1430 ℃

2. FEATURE
No lube, no processed, low ball sediment blown fiber is the material filled of high temperature

3. PRODUCTION ENGEERING
COM swinging fiber cotton, adopting Flint Clay as the material, melted by resistance furnace, is produced by swinging technology.
HP, HA swinging fiber cotton, adopting HP Alumina, Silica Powder as the material, melted by Resistance Furnace, is produced by swinging technology.
HZ swinging fiber cotton, adopting HP Alumina, silica powder, zircon, melted by resistance furnace, blowing or swinging, is produced by swinging technology.

4. TECHNICAL FEATURE:
Low thermal conductivity and heat capacity
No corrosive material
Good heat insulation and sound absorption

5. APPLICATION:
Raw material of fiber paper and vacuum forming
Raw material of fiber spray paint and castable
Filler material of high temperature furnace
Raw material of fiber textile

Item
COM
ST
HP
HA
HAZ
HZ
Classification Temperature ℃
1100
1260
1260
1360
1360
1430
Working Temperature ℃
＜1000
1050
1100
1200
1200
1350
Fiber diameter
（um）
blowing
2-3
2-3
2-3
2-3
2-3
2-3
swing
3-4.5
3-4.5
3-4.5
3-4.0
3-4.0
3-4.0
Chemical
Composition
(%)
AL2O3
42-44
45-46
47-49
52-55
45-46
39-40
AL2O3+SIO2
96
97
99
99
-
-
AL2O3+SIO2
+ZrO2
-
-
-
-
99
99
ZrO2
-
-
-
-
5-7
15-17
Fe2O3
＜1.2
＜1.0
0.2
0.2
0.2
0.2
Na2O+K2O
≤0.5
≤0.5
0.2
0.2
0.2
0.2